Wang Xiaojing, Li Guoming*, Liu Cong, Xie Sheng, Dong Yuxue. Preparation of Porous Composite Membrane Based on Surface Grafting of Modified Chitosan by Waterborne Polyurethane[J]. Journal of South China Normal University (Natural Science Edition), 2015, 47(1): 38-42. doi: 10.6054/j.jscnun.2014.06.015
Citation: Wang Xiaojing, Li Guoming*, Liu Cong, Xie Sheng, Dong Yuxue. Preparation of Porous Composite Membrane Based on Surface Grafting of Modified Chitosan by Waterborne Polyurethane[J]. Journal of South China Normal University (Natural Science Edition), 2015, 47(1): 38-42. doi: 10.6054/j.jscnun.2014.06.015

多孔水性聚氨酯表面接枝改性硫酸化壳聚糖复合膜的制备

Preparation of Porous Composite Membrane Based on Surface Grafting of Modified Chitosan by Waterborne Polyurethane

  • 摘要: 采用己二异氰酸酯三聚体(HT)、2,4甲苯二异氰酸酯(TDI)、聚乙二醇800为基本原料,以1,4丁二醇、2,2二甲基丙酸和乙二胺为亲水扩链剂,合成了水性聚氨酯(WPU),以CaCO_3作为致孔剂制备多孔WPU膜,并与硫酸化壳聚糖(SCS)接枝,制得多孔WPU/SCS复合膜,探讨了致孔剂的用量对WPU/SCS复合膜孔隙率和吸水率的影响.利用红外光谱仪和光学显微镜对复合膜的结构和形态进行了表征,并通过复钙化时间和动态凝血时间对其血液相容性进行了表征.结果表明,致孔剂CaCO_3使用量为12%时,孔隙率为68.3%,吸水率达112.5%,多孔WPU/SCS复合膜具有较好的血液相容性,是一种理想的生物医用材料.

     

/